| 1. Identificação | ||||
| Tipo de Referência | Artigo em Revista Científica (Journal Article) | |||
| Site | mtc-m21c.sid.inpe.br | |||
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S | |||
| Identificador | 8JMKD3MGP3W34R/3SSG6JB | |||
| Repositório | sid.inpe.br/mtc-m21c/2019/03.08.16.36 (acesso restrito) | |||
| Última Atualização | 2019:03.08.16.36.05 (UTC) simone | |||
| Repositório de Metadados | sid.inpe.br/mtc-m21c/2019/03.08.16.36.05 | |||
| Última Atualização dos Metadados | 2020:01.06.11.42.11 (UTC) administrator | |||
| DOI | 10.1007/s40735-019-0228-6 | |||
| ISSN | 2198-4220 | |||
| Chave de Citação | DalibónPeMoRaTrBr:2019:MeCoBe | |||
| Título | Mechanical and corrosion behaviour of DLC and TiN coatings deposited on martensitic stainless steel  | |||
| Ano | 2019 | |||
| Mês | June | |||
| Data de Acesso | 01 maio 2024 | |||
| Tipo de Trabalho | journal article | |||
| Tipo Secundário | PRE PI | |||
| Número de Arquivos | 1 | |||
| Tamanho | 2189 KiB | |||
| 2. Contextualização | ||||
| Autor | 1 Dalibón, Eugenia L. 2 Pecina, J. Nahuel 3 Moscatelli, Mauro N. 4 Ramírez Ramos, Marco Antonio 5 Trava-Airoldi, Vladimir Jesus 6 Brühl, Sonia P. | |||
| Grupo | 1 2 3 4 LABAS-COCTE-INPE-MCTIC-GOV-BR 5 LABAS-COCTE-INPE-MCTIC-GOV-BR | |||
| Afiliação | 1 Surface Engineering Group, Universidad Tecnológica Nacional (UTN-FRCU) 2 Surface Engineering Group, Universidad Tecnológica Nacional (UTN-FRCU) 3 Surface Engineering Group, Universidad Tecnológica Nacional (UTN-FRCU) 4 Instituto Nacional de Pesquisas Espaciais (INPE) 5 Instituto Nacional de Pesquisas Espaciais (INPE) 6 Surface Engineering Group, Universidad Tecnológica Nacional (UTN-FRCU) | |||
| Endereço de e-Mail do Autor | 1 dalibone@frcu.utn.edu.ar 2 3 4 marco.ramos@inpe.br 5 vladimir.airoldi@inpe.br | |||
| Revista | Journal of Bio- and Tribo-Corrosion | |||
| Volume | 5 | |||
| Número | 2 | |||
| Páginas | e34 | |||
| Histórico (UTC) | 2019-03-08 16:36:29 :: simone -> administrator :: 2019 2020-01-06 11:42:11 :: administrator -> simone :: 2019 | |||
| 3. Conteúdo e estrutura | ||||
| É a matriz ou uma cópia? | é a matriz | |||
| Estágio do Conteúdo | concluido | |||
| Transferível | 1 | |||
| Tipo do Conteúdo | External Contribution | |||
| Tipo de Versão | publisher | |||
| Palavras-Chave | DLC coating TiN coating Mechanical behaviour Corrosion behaviour | |||
| Resumo | The ceramic and carbon coatings such as titanium nitride (TiN) and diamond-like carbon (DLC) coatings are characterised by good mechanical properties and chemical inertia. The objective of this work is to compare the wear, friction, adhesion and corrosion behaviour of commercial TiN and DLC coatings deposited on AISI 420 stainless steel, by plasma-assisted techniques. The microstructure of the coatings was characterised by optical and electronic microscopy and X-ray diffraction. The hardness and Youngs modulus were measured by nanoindentation. Pin-on-disk, fretting and abrasive wear tests were performed. Adhesion was evaluated by means of Scratch Test and Rockwell C Indentation. The corrosion behaviour was evaluated by Salt Spray Fog and electrochemical tests in chloride solutions. The thickness of both coatings was between 1 and 1.5 µm. The hardness was 26 GPa and 34 GPa for DLC and TiN coating, respectively. The results showed that the TiN coatings presented better abrasive wear resistance than the DLC coatings; however, the latter was more resistant to the pinon-disk test, fretting and it had a lower friction coefficient. Both coatings showed far better wear resistance than the untreated steel. Finally, TiN coatings had better adhesion to the substrate than DLC coatings, proved in both tests. Regarding the corrosion behaviour, both coatings exhibited acceptable corrosion resistance in the Salt Spray Fog Test, but only the DLC coatings had both nobler corrosion potential and higher breakdown potential than the TiN coatings in electrochemical tests. | |||
| Área | FISMAT | |||
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > Mechanical and corrosion... | |||
| Conteúdo da Pasta doc | acessar | |||
| Conteúdo da Pasta source | não têm arquivos | |||
| Conteúdo da Pasta agreement |
| |||
| 4. Condições de acesso e uso | ||||
| Idioma | en | |||
| Arquivo Alvo | dalibon_mechanical.pdf | |||
| Grupo de Usuários | simone | |||
| Grupo de Leitores | administrator simone | |||
| Visibilidade | shown | |||
| Permissão de Leitura | deny from all and allow from 150.163 | |||
| Permissão de Atualização | não transferida | |||
| 5. Fontes relacionadas | ||||
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 | |||
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.24.19.30 6 | |||
| Divulgação | SCOPUS | |||
| Acervo Hospedeiro | urlib.net/www/2017/11.22.19.04 | |||
| 6. Notas | ||||
| Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project resumeid rightsholder schedulinginformation secondarydate secondarykey secondarymark session shorttitle sponsor subject tertiarymark tertiarytype url | |||
| 7. Controle da descrição | ||||
| e-Mail (login) | simone | |||
| atualizar | ||||